7129 aluminium alloy

Aluminium zinc alloy

Aluminium 7129 alloy is a heat treatable wrought alloy.[1]

Chemical composition

Element[1] Weight Percentage (%)
Aluminum 90.9 - 94
Zinc 4.2 - 5.2
Magnesium 1.3 - 2
Copper 0.50 - 0.90
Iron ≤ 0.30
Titanium ≤ 0.050
Vanadium ≤ 0.050
Gallium ≤ 0.030
Silicon ≤ 0.15
Chromium ≤ 0.10
Manganese ≤ 0.10
Remainder (each) ≤ 0.050
Remainder (total) ≤ 0.15

Properties

Properties Metric
Density[1] 2.78 g/cm3
Youngs modulus[2] 69 GPa
Elongation at Break[2] 9.0 % to 9.1 %
Fatigue Strength[2] 150 to 190 MPa
Shear Modulus[2] 26 GPa
Shear Strength[2] 250 to 260 MPa
Tensile Strength: Ultimate (UTS)[2] 430 MPa
Specific Heat Capacity[2] 880 J/kg-K
Thermal Conductivity[2] 150 W/m-K

Applications

  1. Aircraft manufacturing sector[1]

References

  1. ^ a b c d "7129 aluminum alloy". 9 May 2013. Archived from the original on 2020-12-02.
  2. ^ a b c d e f g h "7129 aluminum properties". Archived from the original on 2016-11-15.

External links

  1. Comparison of 6061 and 7129 alloy
  2. http://www.matweb.com/search/datasheet.aspx?matguid=d62fafde9ffe4ef68614c5e2ab5869e5
  • v
  • t
  • e
Aluminium alloys
Introduction
  • Aluminium
  • Aluminium alloys
  • History of aluminium
Al 1000 series (pure)
  • 1050
  • 1060
  • 1070
  • 1100
  • 1145
  • 1199
  • 1200
  • 1230
  • 1350
  • 1370
  • 1420
  • 1421
  • 1424
  • 1430
  • 1440
  • 1441
  • 1445
  • 1450
  • 1460
  • 1461
  • 1464
  • 1469
Al-Cu 2000 series
  • 2004
  • 2011
  • 2014
  • 2017
  • 2020
  • 2024
  • 2025
  • 2029
  • 2036
  • 2048
  • 2055
  • 2080
  • 2090
  • 2091
  • 2094
  • 2095
  • 2097
  • 2098
  • 2099
  • 2124
  • 2195
  • 2196
  • 2197
  • 2198
  • 2218
  • 2219
  • 2224&2324
  • 2297
  • 2319
  • 2397
  • 2519
  • 2524
  • 2618
Al-Mn 3000 series
Al-Si 4000 series
  • 4006
  • 4007
  • 4015
  • 4032
  • 4043
  • 4047
  • 4543
Al-Mg 5000 series
Al-Mg-Si 6000 series
Al-Zn 7000 series8000 series (misc.)
  • 8006
  • 8009
  • 8011
  • 8014
  • 8019
  • 8025
  • 8030
  • 8090
  • 8091
  • 8093
  • 8176
Named alloys