6010 aluminium alloy
6010 Aluminium alloy has Aluminium as the major element, and has silicon, magnesium, manganese and zinc as minor elements. [1]
Chemical composition
Element [1] | Weight Percentage (%) |
---|---|
Aluminum | 97.3 |
Silicon | 1 |
Magnesium | 0.80 |
Manganese | 0.5 |
Copper | 0.35 |
Mechanical Properties
Properties [1] | Metric |
---|---|
Tensile strength | 290 MPa |
Yield strength | 170 MPa |
Elastic modulus | 69 GPa |
Poisson's ratio | 0.33 |
Elongation at break | 24% |
Thermal Properties
Thermal Properties [2] | Metric |
---|---|
CTE, linear | 21.5 μm/m-°C @Temperature -50.0 - 20.0 °C |
Specific Heat Capacity | 0.890 J/g-°C |
Thermal Conductivity | 151 W/m-K |
Melting Point | 585 - 649 °C |
Solidus | 585 °C |
Liquidus | 649 °C |
References
- ^ a b c "6010 Aluminium alloy". 25 April 2013. Archived from the original on 2020-08-07.
- ^ "6010 thermal properties". Archived from the original on 2021-01-21.
- v
- t
- e
Aluminium alloys
- Aluminium
- Aluminium alloys
- History of aluminium
- 1050
- 1060
- 1070
- 1100
- 1145
- 1199
- 1200
- 1230
- 1350
- 1370
- 1420
- 1421
- 1424
- 1430
- 1440
- 1441
- 1445
- 1450
- 1460
- 1461
- 1464
- 1469
- 4006
- 4007
- 4015
- 4032
- 4043
- 4047
- 4543
- 8006
- 8009
- 8011
- 8014
- 8019
- 8025
- 8030
- 8090
- 8091
- 8093
- 8176
- Aluminium–lithium alloys
- AlBeMet
- Alclad
- Alnico
- AlSiC
- Alumel
- Aluminium granules
- Alusil
- Birmabright
- Devarda's alloy
- Duralumin
- Hiduminium (aka R.R. alloys)
- Hydronalium
- Italma
- Lo-Ex
- Magnalium
- Magnox (alloy)
- MKM steel
- Nickel aluminide
- Aluminium–scandium alloys
- Y alloy
- Al-Ca composite
- Hypereutectic piston
- Aluminium bronze
- AlSi10Mg